MAGNETIC-PROPERTIES OF NDMN6SN6 AND SMMN6SN6 COMPOUNDS FROM SUSCEPTIBILITY MEASUREMENTS AND NEUTRON-DIFFRACTION STUDY

Citation
B. Malaman et al., MAGNETIC-PROPERTIES OF NDMN6SN6 AND SMMN6SN6 COMPOUNDS FROM SUSCEPTIBILITY MEASUREMENTS AND NEUTRON-DIFFRACTION STUDY, Journal of alloys and compounds, 252(1-2), 1997, pp. 41-49
Citations number
27
Categorie Soggetti
Chemistry Physical","Metallurgy & Metallurigical Engineering","Material Science
ISSN journal
09258388
Volume
252
Issue
1-2
Year of publication
1997
Pages
41 - 49
Database
ISI
SICI code
0925-8388(1997)252:1-2<41:MONASC>2.0.ZU;2-L
Abstract
Investigations by susceptibility measurements and neutron diffraction experiments have been performed on the ternary stannides NdMn6Sn6 and SmMn6Sn6 of HoFe6Sn6- and HfFe(6)Ge6-type structure, respectively. In these structures, each of the rare earth and manganese atoms is succes sively distributed in alternate layers with the sequence Mn-R-Mn-Mn-R- Mn. Owing to the manganese atom coordination of the rare earth, they a ppear closely related to the CaCu5- and ThMn12-type structures. NdMn6S n6 and SmMn6Sn6 are ferromagnetic below 357 and 405 K respectively. Tw o additional magnetic transitions related to the spin reorientation pr ocess are undergone in NdMn6Sn6 at 135 and 35 K. A neutron diffraction study of NdMn6Sn6 shows that both the rare earth and manganese sublat tices order simultaneously above room temperature. The magnetic struct ure of NdMn6Sn6 consists of ferromagnetically coupled Mn and Nd ferrom agnetic (100) layers (i.e. positive Nd-Mn interaction). In the tempera ture range 135-35 K, the moment direction is along the a-axis whereas an easy plane occurs at 300 and 2 K with mu(Nd)=3.30(5) mu(B) and mu(M n)=2.39(4) mu(B). The results are discussed and compared with those pr eviously obtained for the parent NdMn6Ge6 and RMn6Sn6 (R=Tb-Er, Lu, Y, Sc) compounds.