Af. Cobeno et al., Physical properties of nearly zero magnetostriction Co-rich glass-coated amorphous microwires, J MATER RES, 14(9), 1999, pp. 3775-3783
Magnetic and mechanical properties of Go-rich amorphous microwires of nomin
al compositions (Co1-xMnx)(75)Si-10 B-15 (0.08 < x < 0.11) and Co56.5Fe6.5N
i10B16Si11 with nearly zero magnetostriction constant have been studied. Dr
astic changes of the hysteresis loop with the decrease of x from rectangula
r to flat shape were observed at x < 0.1, while the Co56.5Fe6.5Ni10B16Si11
microwire showed rectangular hysteresis loops. Compositions with x greater
than or equal to 0.1 have small but positive magnetostriction constant whil
e negative lambda(s) values have been observed at x less than or equal to 0
.09, indicating rectangular character of the hysteresis loop in samples wit
h nearly zero and even for small negative lambda(S). External stress depend
ence of switching field, H*, showed an increase of H* with sigma for sample
s with x = 0.11 and a decrease of H* with sigma for x = 0.1. Besides, micro
wires of the same composition but with different dimensions showed differen
t H*(sigma) dependencies.