M. Shibata et al., Magnetic properties of metal layer deposited by reduction of metal ions contained in polymer with applying magnetic field, J POLYM R, 7(1), 2000, pp. 57-61
Metal layer was deposited by the reduction of NiCl2 and CoCl2 in polyacrylo
nitrile film after applying an external magnetic field in directions parall
el and perpendicular to the surface of the film; the magnetic properties of
the metal-deposited film were investigated. When the parallel magnetic fie
ld was applied, the values of coercivity (H-c), remanent flux density (B-r)
and maximum flux density (B-delta) increased regardless of the composition
of the metal ions, compared with the case without the application of the m
agnetic field. From the scanning electron micrographs and X-ray diffraction
analyses, it was shown that the growth of crystalline orientation in the d
eposited metals was enhanced by applying a parallel magnetic field.