Yx. Huang et H. Zhang, Characteristics of a low-cobalt AB(5)-type hydrogen storage alloy obtainedby a gas-atomization processing, J ALLOY COM, 305(1-2), 2000, pp. 76-81
A low-cobalt ML(NiCoMnAlSnSi)(5) ahoy was prepared by a gas atomization pro
cessing. The discharge capacity of the atomized powder was around 150 mAh/g
which could be increased to about 200 mAh/g after heat treated at 850 degr
ees C for 6 h. A good activation performance was observed for the atomized
powder particularly when the particle size was small. The small particle si
ze and the presence of minor phases were responsible for the quick activati
on. The rate capability of the atomized powder was also improved by heat tr
eatment. (C) 2000 Elsevier Science S.A. All rights reserved.