Lead tungstate PbWO4 single crystals were grown from sodium metasilicate ge
l and water solutions of lead acetate and sodium tungstate as the reagents.
Crystals grown were several micrometer in size and by X-ray diffraction me
asurements it was determined that they are only of the scheelite structure.
No evidence of lead tungstate low temperature modification - raspite - was
found. The emission properties of crystals were measured over the temperat
ure interval 80 to 300 K and it was found that they are similar to those in
PbWO4 crystals grown by the Czochralski method.