H-j(c), J(r) and (BH)(max) relationship in PrFeB melt spun alloys

Citation
G. Mendoza-suarez et al., H-j(c), J(r) and (BH)(max) relationship in PrFeB melt spun alloys, J MAGN MAGN, 218(1), 2000, pp. 97-102
Citations number
12
Categorie Soggetti
Apllied Physucs/Condensed Matter/Materiales Science
Journal title
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
ISSN journal
03048853 → ACNP
Volume
218
Issue
1
Year of publication
2000
Pages
97 - 102
Database
ISI
SICI code
0304-8853(200007)218:1<97:HJA(RI>2.0.ZU;2-X
Abstract
H-j(o), J(r) and (BH)(max) correlations were experimentally studied for a s eries of PrxFe94-xB6 alloys, with x ranging from 6 to 20 at%. The results s how that the variation of the Pr content and the casting parameters yielded to H-j(c) ranging from values near 0 to similar to 2200 kA/m. J(r) increas ed at the expense of H-j(c) in agreement with some theoretical investigatio ns related to J(r)/H-j(c) relationship. This behaviour changed for H-j(c) v alues lower than similar to 200kA/m, where J(r) and H-j(c) diminish togethe r. (BH)(max) showed a similar behaviour to J(r) up to values of H-j(c) simi lar to 450kA/m (30% alpha-Fe) where a maximum was observed and then a decre ase with reducing H-j(c). The results are analysed and discussed based on t heoretical and experimental investigations carried out by some other worker s and compared with results reported for the NdFeB system. (C) 2000 Elsevie r Science B.V. All rights reserved.