Preferential sputtering induced stress domains and mesoscopic phase separation on CaF2(111)

We report the formation of novel mesoscopic two-dimensional bubble structur es coexisting with nanometer-scale, two monolayer-high, meandering islands of characteristic separation similar to 11nm on CaF2(111) surfaces exposed to glancing incidence ion beam irradiation (4 degrees, 4.5 keV Ar+). The is land and bubble structures can be explained, respectively, by nanoscale str ess domain related local selfordering of a single calcium adlayer on phase- separated F- (fluorine ion) and F-center (color center) terminated mesoscop ic domains.