S. Sathyamurthy et K. Salama, Chemical solution deposition of highly oriented strontium titanate buffer layers for coated conductors, SUPERCOND S, 13(7), 2000, pp. L1-L3
Highly oriented strontium titanate films have been processed on single-crys
tal lanthanum aluminate and on textured nickel substrates using solution de
position. Precursor solutions of strontium acetate and titanium Iv butoxide
in acetic acid and methanol were deposited on substrates using spin coatin
g and heat treated in a reducing atmosphere in a single stage to yield text
ured strontium titanate films. A dense crack-free microstructure with a gra
in size of the order of 100 nm was achieved along with a texture of the sam
e order as the underlying substrate. These results offer promise for scalab
le processing of buffer layers on textured nickel.