Ultrasonic investigation of Pd39Ni10Cu30P21 bulk metallic glass upon crystallization

Acoustic velocities of Pd39Ni10Cu30P21 bulk metallic glass (BMG) are measur ed by an ultrasonic technique upon annealing. The elastic constants and the Debye temperature are obtained. A large softening of the transverse phonon is exhibited in the as-quenched BMG relative to its crystallized state. Up on crystallization, the shear modulus and the Debye temperature increase by similar to 30% and similar to 12%, respectively; however, the density incr eases by only similar to 0.6%. Some anomalous acoustic and elastic behavior s are observed near the glass transition temperature and in the supercooled liquid region of the BMG. The anomalies are explained with regard to the s tructural changes. (C) 2000 American Institute of Physics. [S0003-6951(00)0 4634-9].