A. Matlis et al., Low-threshold and high power lambda similar to 9.0 mu m quantum cascade lasers operating at room temperature, APPL PHYS L, 77(12), 2000, pp. 1741-1743
We report a low threshold current density and high power for lambda similar
to 9 mu mAlInAs/GaInAs quantum cascade lasers operating at room temperatur
e. The threshold current density is 1.95 kA/cm(2) at 300 K and 0.61 kA/cm(2
) at 80 K for 5 mu s pulses at 200 Hz repetition rate. The peak output powe
r is 700 mW at room temperature and 1.3 W at 80 K per two facets for cavity
length is 3 mm with a stripe width of 20 mu m. The characteristic temperat
ure T-0 is 185 degrees C. The slope efficiency is 450 and 800 mW/A at 300 a
nd 80 K, respectively. In continuous wave operation, the output power is mo
re than 150 mW at 80 K and 25 mW at 140 K. This high performance was achiev
ed by improving the material growth and processing technology. (C) 2000 Ame
rican Institute of Physics. [S0003-6951(00)01038-X].