High frequency resonance features of giant magnetoresistance multilayers

High frequency resonance technique was applied to study of magnetic multila yer Co/Cu films possess the giant magnetoresistance. The results of the fer romagnetic resonance study in 60GHz-80GHz and 10GHz bands revealed low temp erature changes of g-factor after annealing and a Very small value of high frequency saturation magnetization. An abrupt change of the specimen impeda nce was registered in low field low field range for 10GHz. The static magne tic characteristics as hysteresis and magnetoresistance loops were obtained at room temperature for the planar orientation of external magnetic field.