M. Bououdina et al., Study of the ZrCr0.7Ni1.3 multiphased system under hydrogen pressure by in-situ neutron diffraction, J ALLOY COM, 311(2), 2000, pp. 248-251
Both X-ray and neutron diffraction Rietveld analyses show that the as-cast
ZrCr0.7Ni1.3 alloy crystallises with the C15-type Laves phase type structur
e, with the presence of >30 wt.% Zr7Ni10 and a few weight percent chromium.
After annealing at 1373 K, we observed the disappearance of chromium metal
and a reduction by more than half of Zr7Ni10. P-C-T measurements performed
on the as-cast material show an absorption capacity of about 0.9 H/AB(2) a
t 323 K and under P = 10 bar. In-situ neutron diffraction experiments perfo
rmed at 323 It under deuterium gas pressure reveal that, after full hydroge
nation of the sample, the Zr7Ni10 phase transforms into an amorphous phase,
but recrystallises under vacuum when the temperature is raised above 373 K
. (C) 2000 Elsevier Science S.A. All rights reserved.