Sx. Mcfadden et al., Observations of low-temperature superplasticity in electrodeposited ultrafine grained nickel, MATER LETT, 45(6), 2000, pp. 345-349
In this study, superplasticity was obtained from electrodeposited nanocryst
alline nickel at 350 degrees C, which is 0.36 of the melting point T-m. A m
aximum elongation of 895% was obtained at 0.4 T-m, which is a large reducti
on in temperature and increase in elongation over the previously reported b
est result for nickel. (C) 2000 Elsevier Science B.V. All rights reserved.