H. Iwasaki et al., THE ROLE OF LIQUID-PHASE IN CAVITATION IN A SI3N4P AL-MG-SI COMPOSITEEXHIBITING HIGH-STRAIN-RATE SUPERPLASTICITY/, Acta materialia, 45(7), 1997, pp. 2759-2764
Citations number
34
Categorie Soggetti
Material Science","Metallurgy & Metallurigical Engineering
Cavitation was quantitatively investigated at 8 MPa and 833 K for a hi
gh-strain-rate superplastic Si3N4p/Al-Mg-Si composite, where the testi
ng temperature of 833 K was slightly above the onset temperature for p
artial melting. Most of the cavities were very small (less than or equ
al to 1 mu m), and cavity development was not significant. Based on a
theoretical analysis, when stress concentrations around reinforcements
are relaxed by the presence of a liquid phase, excessive cavity devel
opment is suggested to be limited. This view is in agreement with the
experimental results. (C) 1997 Acta Metallurgica Inc.