Structural and dielectric properties of sol-gel derived PLZT (x/60/40)

Polycrystalline samples of (Pb1-zLaz)(Zr0.60Ti0.40)(1-z/4)O-3 (where z = 0. 00, 0.05, 0.09, 0.12, 0.14 mol %) (abbreviated as PLZT) were synthesized th rough acetate-alkoxide sol-gel route. The formation and existence of differ ent crystallographic phases as a function of z was checked through X-ray, T EM, SEM and dielectric studies. The diffuse phase transition (DPT) was obse rved in PLZT with higher concentration of La (i.e., for z = 0.00 to 0.12), but for z = 0.14, the compound did not show any phase transition.