The grain size dependence of the intergrain critical current density J(c)(i
nter) in untextured YBa(2)Cu(3)Ox ceramics determined both in low and high
fields was investigated. Whereas in low fields J(c)(inter) decreases with t
he mean grain size phi (g), it is one order of magnitude higher and increas
es with phi (g) in high fields.