Ceramic tapes, containing Al2O3-25 wt pet TiB2(B) and Al2O3-25 wt pet
nano-TiC (c), have been obtained by tape casting process. Numerous tap
es (about 60 similar to 80 tapes) were prepared by stacking in turn th
e composition (B) and (C), laminating under 10 MPa pressure, eliminati
ng the solvent and burning out the polymer additives. The final green
bodies were hot pressed at 1750 degrees C and 30 MPa. The composite ha
s a bending strength of 568 MPa and a fracture toughness of 5.8 MPa.m(
1/2). SEM analysis exhibits that Al(2)O3 particle growth was inhibited
by TIC particles in C, but TiB2 particles could not hinder Al2O3 grow
th in B. The curves of GTA indicates that all organic additives could
be removed completely above 600 degrees C.