The changes produced in the dielectric permittivity, the transverse piezoel
ectric coefficient, the k(31) coupling factor, the s(11)(E) elastic complia
nce and the mechanical quality factor of PZT-4D hard piezoceramics by heati
ng have been investigated. The ceramics were then repoled, and the reversib
le and irreversible components of the changes quantified. The results showe
d that depolarisation began at 150 degreesC. A high level of poling was ret
ained even after heating at 300 degreesC (d(31) = -83 x 10(-12) C N-1 and k
(31) = 0.225), only 20 degreesC below the transition temperature. However,
a significant irreversible degradation of the mechanical quality factor, Q(
m), occurred at a temperature as low as 100 degreesC. Experiments on thinne
d specimens showed that the degradation of Q(m) took place in the Ag doped
layer produced by the electrodes. Indentation surface cracks were also intr
oduced into the ceramics to investigate the behaviour of cracks during the
thermal treatments. (C) 2000 Elsevier Science Ltd. All rights reserved.