O. Haruyama et al., THERMAL STABILITIES OF SOME GLASSY METALS WITH A WIDE SUPERCOOLED LIQUID REGION, Materials science & engineering. A, Structural materials: properties, microstructure and processing, 226, 1997, pp. 209-212
The thermal stability of a Zr60Al15Ni25 glassy metal was investigated
mainly by electrical resistance measurements. In particular, attention
was paid to the influence of thermal histories, i.e., the sample prep
aration condition and the atmosphere during measurement of physical pr
operties. The glass-transition phenomenon was distinctly detected from
the change in the electrical resistance with increasing temperature.
The electrical resistance behavior of a Pd58Ni25Si17 glassy metal arou
nd its glass-transition temperature was also examined for comparison.
A similar change in the electrical resistance associated with the glas
s transition was also observed for this Pd-based glassy metal. It is,
therefore, presumed that the electron transport property changes aroun
d the glass-transition temperature. Both the glass-transition temperat
ure and the crystallization temperature were almost independent of the
thermal history of their samples. However, the temperature derivative
of the electrical resistance is significantly dependent on the therma
l history. (C) 1997 Elsevier Science S.A.