ZnO nanowires were mass produced using a physical vapor deposition approach
. The ZnO nanowire monocrystallites have an average diameter around 60 nm a
nd length up to a few micrometers. The unidirectional growth of the ZnO nan
owires was controlled by the conventional vapor-liquid-solid mechanism. Int
ensive UV light emission peaked around 3.27 eV was observed at room tempera
ture, which was assigned to emission from free exciton under low excitation
intensity. The observed room temperature UV emission was ascribed to the d
ecrease in structure defects as compared to bulk ZnO materials, and in part
icularly to the size effect in the ZnO wires. (C) 2001 American Institute o
f Physics.