In this work, we performed a three-dimensional analysis of YBa2Cu3Ox/Ag sam
ples microstructure, especially with regard to silver distribution. By this
way, we study thoroughly the correlation between the morphology and the el
ectrical behaviour of the samples varying the silver content We were able t
o show that the percolation limit of silver in YBCO is around 7.5 wt.%. We
pointed out that the silver drops tends to disorder the system at high conc
entration, suggesting the opportunity of texturing under uniaxial pressure.