The SrMn1-xFexO3-delta (x = 1/3, 1/2, 2/3) phases have been prepared and ar
e shown by powder X-ray and neutron (for x = 1/2) diffraction to adopt an i
deal cubic perovskite structure with a disordered distribution of transitio
n-metal cations over the six-coordinate B-site. Due to synthesis in air, th
e phases are oxygen deficient and formally contain both Fe3+ and Fe4+. Magn
etic susceptibility data show an antiferromagnetic transition at 180 and 14
0 K for x = 1/3 and 1/2, respectively and a spin-glass transition at 5, 25,
45 K for x = 1/3, 1/2 and 2/3, respectively. The magnetic properties are e
xplained in terms of super-exchange interactions between Mn4+, Fe(4+delta) and Fe(3+epsilon)+. The XAS results for the Mn-sites in these compounds in
dicate small Mn-valence changes, however, the Mn-pre-edge spectra indicate
increased localization of the Mn-e(g) orbitals with Fe substitution. The Mo
ssbauer results show the distinct two-site Fe(3+epsilon)+/Fe(4+delta)+ disp
roportionation in the Mn- substituted materials with strong covalency effec
ts at both sites. This disproportionation is a very concrete reflection of
a localization of the Fe-d states due to the Mn-substitution. (C) 2000 Edit
ions scientifiques et medicales Elsevier SAS. All rights reserved.