The SEM observation in situ of monotonic and cyclic deformed structure in T
i-2Al-2.5Zr alloy was performed. The regularity of slippage, crack nucleati
on, propagation and the typical dislocation configuration were also investi
gated. The twin and twist play an important role in maintaining homogeneous
deformation in the final plastic deformation stage.