Gh. Wu et al., Effect of thermal cycling treatment on microstructure and mechanical properties of AlNp/2024Al composite, J MAT SCI T, 17(1), 2001, pp. 61-62
The AlNp/2024 composite with a high volume fraction (50%) was fabricated by
squeeze casting. Its mechanical properties were investigated by tensile te
sts at ambient temperature and the microstructure was observed by a transmi
ssion electron microscope (TEM). It was indicated that after six thermal co
oling cycles treatment the AlN/2024AI composite exhibited higher elastic li
mit (sigma (0.01)), tensile strength (UTS) and elastic modulus (E). TEM obs
ervation showed that there was higher dislocation density both in the matri
x and the particle. delta' phase is the mainly precipitate.