Nanocrystalline WS, was prepared by the reaction of elemental sulfur and so
dium tungstate (or calcium tungstate) in an aluminum chloride molten-salt.
XPS, XRD and TEM indicated that the product was 2H-WS2 nanoparticles with s
ize of 20-50 nm and irregular morphology.