In this paper, the procedure of preparation of graphite-Teflon composi
te electrode (GTE) by coating was investigated. The coating consisted
of a solid mixture 2.5 g(graphite 45%, Teflon 45% and PVC 10%) mixed w
ith a solvent(THF: DMF = 1:4 in volume) 0.8 mL. Copper wires(phi = 0.7
mm) were coated by the coating and heated at 200 degrees C for 5 min,
and the GTEs were finished. They could be modified and changed into o
ther metallic Teflon composite electrode only by electroplating in cor
respondent plating bath, such as mercury- cobalt- or copper- Teflon co
mposite electrode. They had been applied to flow injection analysis by
techniques of electrochemistry successfully.