Calcium phosphate invert glasses, which contain P2O72- and PO43- ions, have
been prepared via the addition of a small amount of TiO2. The formation of
bonelike calcium phosphate apatite on the surface of the phosphate invert
glasses was examined in simulated body fluid (SBF) at a temperature of 37 d
egreesC, Soaking for 20 d resulted in the deposition of leaflike apatite pa
rticles on 6CaO . 3P(2)O(5). TiO2 invert glass (based an molar ratio). The
glass had much-greater chemical durability against SBF, in comparison with
a metaphosphate glass; P ions were not dissolved exceessively from the 6CaO
. 3P(2)O(5). TiO2 glass, so the apatite formation was not suppressed.