Ion-beam irradiation of Cu and a Cu-Ni alloy single-crystal specimens: Proposed atom movement mechanism - art. no. 100101

Rutherford backscattering and channeling measurements have been applied to study deep radiation damage and depth profile of implanted Au atoms in pure Cu and Cu-1 at. % Ni alloy single-crystal specimens, which were irradiated off axis at room temperature by 300 keV Au+ ions to a dose of 2 x 10(16) i ons/cm(2). The damage range and depth range of the implanted Au atoms in th e specimens of pure Cu were strikingly deeper than those in the specimens o f Cu-1 at. % Ni alloys, respectively. An atom movement mechanism in solids under ion beam irradiation is proposed as the origin of the observed result .