Disruption erosion tests on La2O3 containing and pure tungsten materials we
re performed by the electron beam irradiation facility. As a result, it was
found that the disruption erosion of La2O3 - W evaluated from the weight l
oss was three times larger than that of pure - W. The surface observations
suggest that the splashing of the melted layer during the electron beam irr
adiation occurs only for the La2O3 - W, which results in the larger weight
loss in disruption erosion. This is considered to be due to the lower melti
ng point of the added La2O3.