New Liquid crystalline materials with low processing temperature, whilst ma
intaining the mechanical properties characteristic of the liquid crystallin
e polymers, were sought by blending Rodrun 5000 and Rodrun 3000. After dire
ct injection moulding, the solid blends appeared as miscible. The crystalli
zation from the melt was hindered by the presence of the other component, b
ut the minimum processing temperature of Rodrun 5000 clearly decreased as a
consequence of the presence of Rodrun 3000. This decrease was not at the c
ost of a decrease in the overall mechanical properties. It should be noted
that, unlike in thermoplastics blends, in liquid crystal polymer (LCP) blen
ds the miscibility level influences the modulus values. Immiscibility leads
to clear positive synergisms in the values of the modulus of elasticity an
d also in the tensile strength, that are not seen in miscible LCP blends.