Solid state F-19 NMR determination of new structure formation in FEP following radiolysis at 300 and 363 K

The radiation chemistry of FEP copolymer with a mole fraction TFE of 0.90 h as been studied using Co-60 gamma -radiation at temperatures of 300 and 363 K. New structure formation in the copolymers was analysed by solid state F -19 NMR. New chain scission products were the principal new structures foun d. The G-value for the formation of new -CF3 groups was 2.2 and 2.1 for the radiolysis of FEP at 300 and 363 K, respectively, and the G-value for the loss of original -CF3 groups was G(-CF3) = 1.0 and 0.9 at these two tempera tures, respectively. There was a nett loss of -CF- groups on irradiation, w ith G(-CF) of 1.3 and 0.9 at 300 and 363 K, respectively. (C) 2001 Elsevier Science Ltd. All rights reserved.