Ten volume percent of Al2O3-TiC ceramic particle reinforced Al 5083 and Al
6061 alloy composites were successfully fabricated with high strength by co
mbining twin rolling, a newly devised stone mill type crushing and hot extr
uding. Crushing and composing procedures are enlightened in this work. Both
composites showed high UTS, although, Al 5083 alloy composites were effect
ively strengthened by the rapid solidification, whereas ill 6061 composite
by heat treating. No reaction product was found to firm between the matrix
and reinforcement interfaces, due to no severe thermal exposure of this pro
cess. (C) 2001 Elsevier Science B.V. All rights reserved.