Sy. Chang et al., Effect of heat treatment on tensile properties of component with macro-interface between unreinforced magnesium and composite, MATER TRANS, 42(6), 2001, pp. 1035-1041
The microstructural and mechanical characteristics of component with the ma
cro-interface between unreinforced magnesium and composite manufactured by
squeeze casting were determined. The effect of thermal cycling on the tensi
le properties of the component with the macro-interface, which is a potenti
al site of cyclic stress formation, was investigated. The macro-interface h
as diffuse interface characteristics; its thickness is about 7-10 mum. A re
action product was formed near the macro-interface. It has been found that
the component are weaker than pure magnesium, and the tensile strength of t
he component decreases with thermal cycling as a function of both the numbe
r of thermal cycles and DeltaT. The fracture behavior was evaluated by the
study of fracture surfaces on both sides of the component fractured at the
macro-interface.