Cement mortar was modified using recycled acrylonitrile butadiene styrene (
ABS) in powder form. Mixtures with polymer-cement ratios of 8, 15, and 25 w
t.% were investigated for changes in compressive properties and adhesion to
steel rebar. Compressive tests indicated an increase in Young's modulus fo
r samples with 8% and 15% ABS. Adhesion strength to the steel rebar decreas
ed on adding the ABS. However, when the ABS was treated with maleic anhydri
de, an increase in adhesion strength was obtained. The decrease in adhesion
of the untreated ABS-modified cement to steel was attributed to the disrup
tion of the interface between the cement mortar and steel rebar. Scanning e
lectron microscopy (SEM) indicated changes in the cured cement with additio
n of ABS. Gas adsorption measurements of pore size distribution indicated a
n increase in pore volume of the 8 and 15 wt.%-containing cement mortar. (C
) 2001 Elsevier Science Ltd. All rights reserved.