Mg0.5Ti2(PO4)(3) having NASICON-lattice was prepared by sol-gel method and
evaluated as a cathode material for magnesium cells. The crystalline phase
could be successfully obtained after heating at 600 degreesC. Electrochemic
al magnesium insertion from a propylene carbonate solution into this host w
as found possible and one Mg2+ ion could be accommodated per unit formula.
However, the magnesium insertion process was under kinetic control of Mg2diffusion due to the low mobility of Mg2+ in this host. (C) 2001 Elsevier S
cience BN. All rights reserved.