D. Kuscer et al., Correlation between the defect structure, conductivity and chemical stability of La1-ySryFe1-xAlxO3-delta cathodes for SOFC, J EUR CERAM, 21(10-11), 2001, pp. 1817-1820
The chemical compatibility of a La1-ySryFe1-xAlxO3-delta cathode and an ytt
ria-stabilised ZrO2 electrolyte (YSZ) was studied for solid-oxide fuel cell
(SOFC) applications. The Al addition to the LaFe1-xAlxO3 reduces the react
ivity with the YSZ associated with increasing tolerance factor. The Sr addi
tion to the LaFe1-xAlxO3 leads to Fe4+ and anion-vacancy formation. The Sr
addition hinders the formation of La2Zr2O7, but at y greater than or equal
to 0.2 promotes the formation of SrZrO3 at the La1-ySryFe1-xAlxO3-delta/YSZ
interface. At low p(O-2) the formation of secondary phases is pronounced w
hat could be related to the formation of anion vacancy. (C) 2001 Elsevier S
cience Ltd. All rights reserved.