Sintered ceramics Ca0.9La0.1MnO3-delta were studied on their properties as
cathode active materials in some saline solutions. The ceramics were found
to discharge without any conductive agents such as graphite in the neutral
solutions, although the discharge capacity was lower than that in alkaline
solution. The discharge capacity was the largest in 15% LiCl solution (188
mAh g(-1)).