Fn. Kaputsky et al., METAL CELLULOSE SYNTHESIS OF THIN FIBERS OF YBA2CU3O7-G AND CREATION OF THE COMPONENTS OF HIGH-TEMPERATURE SUPERCONDUCTING EQUIPMENT, Doklady Akademii nauk BSSR, 38(5), 1994, pp. 54-56
First of all the textured fibers of high-temperature superconducting i
ttrium-barium-cuprate and simple articles from them (braids, solenoids
, coils) for cryotronics have been produced using Y-Ba-Cu-salt of tric
arboxylcellulose as a metal-organic precursor. Diamagnetic transition
point (T(c)) was observed at 92 K and the critical current density (J(
c) = 3 10(3) A/cm2) was achieved.