The thermal behaviour of poly(acryloyloxybenzoic acid) (PABA)/nylon 6 (PA6)
blends were investigated by differential scanning calorimetry. Melting poi
nt (T-m) of PA6 depressed with increasing PABA content. When PABA content w
as larger than about 60 wt%, second endotherm, was observed above the T-m (
first endotherm). Wide angle X-ray diffraction analysis suggested that crys
tallinity of PA6 was decreased with increasing PABA content. The second end
otherm could be assigned to the melting of PA6-PABA complex. (C) 2001 Publi
shed by Elsevier Science Ltd.