Lq. Li et al., Activation behaviors of Mg2NiH4 at different hydrogen pressures in hydriding combustion synthesis, INT J HYD E, 26(10), 2001, pp. 1035-1040
For the industrialization of the process of hydriding combustion synthesis
of Mg2NiH4, the activation behaviors Of Mg2NiH4 at different hydrogen press
ures were measured by means of DSC (differential scanning calorimeter) and
XRD (X-ray diffraction). The profiles of heat flow of DSC were very differe
nt at 0.5, 1.0, 2.0 and 4.0 MPa hydrogen pressures within three cycles of t
emperature scanning at a rate of 0.1 K/s in hydriding combustion synthesis
Of Mg2NiH4. It is apparent that an activation behavior existed in the hydri
ding combustion synthesis since the height of DSC peak from the hydriding r
eaction Of Mg2NiH4 increased with the cycling of temperature scanning. The
pressure of hydrogen strongly affected this kind of an activation. The peak
height increased as hydrogen pressure increased. It reached maximum values
after the second cycle of temperature scanning at 4.0 MPa of hydrogen pres
sure and after the third cycle at 2.0 MPa. The patterns of XRD revealed tha
t pure products Of Mg2NiH4 were obtained after the third cycle of temperatu
re scanning at 2.0 MPa of hydrogen pressure and after the second cycle at 4
.0 MPa. These results are significant for developing the industrial process
of hydriding combustion synthesis of hydrogen storage alloy Mg2NiH4 Within
only one temperature scanning without any activation process. (C) 2001 Int
ernational Association for Hydrogen Energy. Published by Elsevier Science L
td. All rights reserved.