Tb. Cao et al., Photoelectric conversion property of covalent-attached multilayer self-assembled films fabricated from diazoresin and fullerol, LANGMUIR, 17(20), 2001, pp. 6034-6036
A novel self-assembly multilayer film was fabricated from fullerenol (C-60(
ONa)(n)) and diazoresin (DR)-a photosensitive polymer on indium-tin-oxide s
ubstrate. The film shows good stability after UV irradiation and has photoe
lectric conversion property, which can be measured in a conventional photoe
lectrochemical cell. The cathodal photocurrent was measured to be about 800
nA/cm(2) for a nine-layer film at 100 mW/cm(2) white light. The photocurre
nt spectroscopy responses coincide with the absorption spectrum of the self
-assembly film, which means that the C-60(ONa)(n)/DR film is responsible fo
r the photocurrent generation.