Nd123 bars were textured using the melt texturing growth process in a verti
cal furnace by the floating zone method. Different applied growth rates wer
e tested, from 1 to 4 mm/h, combined with different secondary phases additi
ons (Nd4Ba2Cu2O5 and Nd3.6Ba2.2Cu1.9Oy,). Nd123 single-domains were obtaine
d independently of the tested conditions and correlation between process co
nditions (composition, growth rate), microstructure and superconducting pro
perties were investigated. An optimized T-c (96 K) with a sharp transition
is obtained without Ar annealing at high temperature generally necessary to
recover the optimal T-c. This attractive result is linked with the process
used. J(c) curves were measured and results were discussed in relation wit
h process conditions. (C) 2001 Elsevier Science B.V. All rights reserved.