A. Bardal et R. Bredesen, On the nano-size intergrowth of Sr4Fe6O13 +/-delta and (Sr1-xLax)FeO3-delta phases in the mixed conductor Sr3.6La0.4Fe6Oz, J MATER SCI, 36(22), 2001, pp. 5357-5367
The microstructures of mixed-conducting Sr4Fe6O13 +/- delta, and Sr3.6La0.4
Fe6Oz (nominal composition) have been studied by electron microscopy. The l
anthanum free material shows a microstructure containing mainly Sr4Fe6O13 /- delta, with some 5 vol% Sr1-yLayFe12O19 embedded as micron-size inclusio
ns. The lanthanum-containing material revealed a significantly different mi
crostructure consisting of similar to 20 vol% micron-size Sr1-yLayFe12O19 e
mbedded in similar to 40 vol% (Sr0.85La0.15)FeO3-delta tetragonal perovskit
e, and similar to 40 vol% of plate-shaped nano-scale intergrowths between (
Sr1-xLax)FeO3-delta and Sr4Fe6O13 +/- delta phases. Domains with dimensions
of 20-50 nm are observed in the tetragonal perovskite when viewed along it
s fourfold axis. From compositional analysis it is concluded that there is
little or no solubility of La in the Sr4Fe6O13 +/- delta phase. The observe
d microstructure is important input in explaining the significant effect of
La addition on the transport properties of Sr4Fe6O13 +/- delta materials.
(C) 2001 Kluwer Academic Publishers.