Solid catalytic growth mechanism of micro-coiled carbon fibers

Micro-coiled carbon fibers were prepared by catalytic pyrolysis of acetylen e with nanosized nickel powder catalyst using the substrate method. The mor phology of micro-coiled carbon fibers was observed through field emission s canning electron microscopy. It was found that the fiber and coil diameter of the obtained micro-coiled carbon fibers is about 500-600 nm and 4-5 mum, respectively. Most of the micro-coiled carbon fibers obtained were regular double carbon coils, but a few irregular ones were also observed. On the b asis of the experimental observation, a solid catalytic growth mechanism of micro-coiled carbon fibers was proposed.