Jk. Kim et al., Effect of aging treatment on heavily deformed microstructure of a 6061 aluminum alloy after equal channel angular pressing, SCR MATER, 45(8), 2001, pp. 901-907
Pre-ECAP solid-solution treatment combined with post-ECAP aging treatment h
as been found to be more effective than pre-ECAP peak-aging treatment in en
hancing the strength of a 6061 Al alloy. An increase of similar to 40% in U
TS and yield stress was obtained in the post-ECAP aged material compared to
the T6 treated commercial 6061 Al alloy. (C) 2001 Acta Materialia Inc. Pub
lished by Elsevier Science Ltd. All rights reserved.