Protonic conduction and defect structures in Sr-doped LaPO4

Protonic conduction and defect structures in Sr-doped LaPO4 (Sr = 0-7 mol%) were investigated by using conductivity, MAS-NMR spectroscopy and FT-Raman spectroscopy measurements. The results of MAS-NMR and FT-Raman spectroscop y measurements revealed that hydrogen phosphate groups, possibly hydrogen p hosphate ions HPO42-, and pyrophosphate ions P2O74- existed in Sr-doped LaP O4 under wet and dry conditions, respectively, in addition to orthophosphat e ions PO43-. Based on these results, we proposed a defect structure model for Sr-doped LaPO4. According to this model, La substitution with Sr leads to formation of P2O74- as intrinsic positive defects, and in wet atmosphere , protons are introduced into the phosphate forming hydrogen phosphate grou ps through the equilibrium between P2O74- and water vapor. The conductivity behavior of Sr-doped LaPO4 versus water vapor and oxygen partial pressures supported this defect structure model. (C) 2001 Elsevier Science B.V. All rights reserved.