NEW HOLE CONFIGURATIONS IN X-IRRADIATED KTIOPO4 CRYSTALS

Electron paramagnetic resonance has been used to study the structure a nd thermostability of oxygen hole centers produced in KTiOPO4 (KTP) cr ystals X-irradiated at 77 K. During the annealing of KTP crystals abov e 160 K the redistribution of charges took place. Four hole centers we re observed at 40 K after the heating of the X-irradiated KTP crystal at different temperatures. The intensity of the hole center 1 decrease d and new hole configurations (center 2 and center 3) appeared in the crystals. The g-matrices were obtained from the angular dependencies o f EPR spectra. The principal g-values for center 1 were 2.0040, 2.0209 , and 2.0437. The principal g-values for centers 2 and 3 were 2.0053, 2.0204, 2.0431 and 2.0035, 2.0183, 2.0628, respectively. The transform ation of Ti3+ spectra indicated that the trivalent titanium ions were involved into the recombination process. Subsequent annealing at tempe ratures above 220 K led to the formation of a new hole center 4 (g(a)= 2.0213, g(b)=2.0236, g(c)=2.0370).