Differential temperature analysis (DTA) in a magnetic field was carried out
for growth of YBa2Cu3O7, in order to investigate the influence of magnetic
fields up to 14T on the melt-textured growth process. The DTA peak for the
heating process, which corresponds to melt transition, was insensitive to
the magnetic field. For the cooling process, however, the peak correspondin
g to crystal formation was shifted to a lower temperature under application
of a magnetic field of 14T. The shift of the DTA peak by a magnetic field
is due to the lowering crystal growth rate by the magnetic field. (C) 2001
Elsevier Science B.V. All rights reserved.