Molecular motion in nanocomposites of poly(ethylene oxide) and montmorillonite

Motion of chains of poly(ethylene oxide) within the interlayer spacing of 2 :1 phyllosilicate/montmorillonite was studied with H-1 and C-13 NMR spectro scopy. Measurements of the H-1 NMR line widths and relaxation times across a large temperature range were used to determine the effect of bulk thermal transitions on polymer chain motion within the nanocomposites. The results were consistent with previous reports of low apparent activation energies of motion. Details of the frequency and geometry of motion were obtained fr om a comparison of the C-13 cross-polarity/magic-angle spinning spectra and relaxation times of the nanocomposite with those of the pure polymer. (C) 2001 John Wiley & Sons, Inc.