Db. Kacedon et al., MAGNETORESISTANCE OF EPITAXIAL THIN-FILMS OF FERROMAGNETIC METALLIC OXIDE SRRUO3 WITH DIFFERENT DOMAIN-STRUCTURES, Applied physics letters, 71(12), 1997, pp. 1724-1726
We have studied the magnetoresistive behavior of epitaxial thin films
of the conductive ferromagnetic oxide SrRuO3 with different domain str
uctures grown on both miscut (001) SrTiO3 and exact (001) LaAlO3 subst
rates. A strong anisotropic magnetoresistance (MR) has been observed i
n the single domain SrRuO3 thin film on miscut (001) SrTiO3 substrate.
In contrast, the SrRuO3 thin film on (001) LaAlO3 substrate shows ide
ntical MR behavior in two orthogonal directions on the film due to the
presence of 90 degrees domains in the plane. For both the films, larg
e negative magnetoresistance effects (similar to 10%) were observed wh
en the current and the applied magnetic field are parallel. This is at
tributed to a reduction in spin fluctuations near T-c and to magnetiza
tion rotation leading to a change in the angle between the current and
magnetization at low temperatures. (C) 1997 American Institute of Phy
sics.